2205 Stainless Steel Pipe

Thickness: 0.5mm-40.0mm
Width: 1000mm, 1219mm
Cold rolling: 2000mm or 2438mm
Advantages: High strength, good impact toughness and good overall and local stress corrosion resistance.
Standard number: ASTM A240/A240M—01

Send Inquiry

Products Description

2205 stainless steel is a duplex stainless steel composed of 21% chromium, 2.5% molybdenum and 4.5% nickel-nitrogen alloy. 2205 stainless steel pipe has high strength, good impact toughness and good overall and local stress corrosion resistance. It is generally used in pulp and paper industry classifiers, bleaching equipment, storage and processing systems, as well as rotating shafts, press rolls, blades, impellers, cargo boxes of ships or trucks, food processing equipment, etc. in high-strength corrosion-resistant environments.

Chemical Composition

C≤0.030 Mn≤2.00 Si≤1.00 p≤0.030 S≤0.020 Cr 22.0～23.0 Ni 4.5～6.5 Mo3.0～3.5 N0.14～0.20 (austenite-ferrite type)

Performance supplement: Main components: 22Cr-5.3Ni-3.2Mo-0.16N; National standards: NAS 329J3L, UNS S32205/S31803, DIN/EN 1.4462, ASTM A240, ASME SA-240; Mechanical properties: Tensile strength: σb≥640Mpa; Elongation: δ≥25%; Typical working conditions: 20% dilute sulfuric acid, below 60℃, annual corrosion rate <0.1mm; Matching welding wire: ER2209.

Chemical composition (JIS G 4305-005) (wt%)

Chemical	C	Si	Mn	P	S	Cr	Ni	Mo	N
Standard	≤0.03	≤1.00	≤2.00	≤0.04	≤0.03	21.0~24.0	4.5~6.5	2.5~3.5	0.08~0.2
generally	0.025	0.6	1.5	0.026	0.001	22.5	5.8	3.0	0.16

Performance (JIS G 4305-2005)

Distinguish	Mechanical properties	Remark	−	−
Ys (Mpa)	Ts (Mpa)	El (%)	Hv	2.0t/2B
≥ 450	≥ 620	≥ 25%	≥ 18	≤ 320
500	670	35%	27	280

Physical properties

Density(g/c㎡)	magnetic	Specific heat (J/g.C)	Thermal conductivity 100C (W/m	Thermal expansion rate 20~100C (10/C)
7.8	yes	0.45	19.0	13.7

Standards

ASTM/ASME...........A240 UNS S32205/S31803

EURONORM...........1.4462 X2CrNiMoN 22.5.3

AFNOR...................Z3 CrNi 22.05 AZ

DIN.........................W. Nr 1.4462

Corrosion resistance

Uniform corrosion

Due to the chromium content (22%), molybdenum (3%) and nitrogen content (0.18%), 2205 has better corrosion resistance than 316L and 317L in most environments.

Local corrosion resistance

The chromium, molybdenum and nitrogen content in 2205 duplex stainless steel makes it highly resistant to pitting and crevice corrosion in oxidizing and acidic solutions.

Stress corrosion resistance

The duplex microstructure of stainless steel helps to improve the resistance of stainless steel to stress corrosion cracking. Under certain temperature, stress, oxygen and chloride conditions, austenitic stainless steel will undergo chloride stress corrosion. Since these conditions are difficult to control, the use of 304L, 316L and 317L is limited in this regard.

Corrosion fatigue resistance

The high strength and corrosion resistance of 2205 duplex steel give it high corrosion fatigue strength. Processing equipment is susceptible to corrosive environments and loading cycles, and the characteristics of 2205 Stainless Steel Pipe are very suitable for such applications.

Morphological Characteristics

Structure

The chemical composition of 2205 achieves an ideal microstructure of 50 α / 50 γ after solution annealing at 1900°/1922°F (1040°/1080°C). Heat treatment above 2000°F may result in an increase in the ferrite content. Like other duplex stainless steels, 2205 alloy is susceptible to the precipitation of intermetallic phases. Intermetallic phases precipitate between 1300°F and 1800°F, with the fastest precipitation rate at 1600°F. Therefore, we need to test 2205 to ensure the absence of intermetallic phases, and the test refers to ASTM A 923.